| Pyrolysis and leaching are the dominant techniques applied in the recycling of waste printed wiring boards (PWBs). Waste PWB pyrolysis is a highly polluting technology and produces brominated pyrolysis oils in addition to hydrogen bromide (HBr) gas. Moreover, leaching as a treatment process of waste PWBs is not well investigated. In this work, the pyrolysis of waste PWBs has been studied with the aim of reducing the amount of brominated oils and HBr gas evolved.;The effects of powder inorganic chemicals (CaO, CaCO3, Fe 2O3, Al2O3, Y-Zeolite, and ZSM-5) additions on the pyrolysis of waste PWBs has been studied through experiments using a thermogravimetric-differential thermal analyzer connected to a mass spectrometer (TG-DTA-MS) and in a tube furnace at 900 °C. It has been shown that the kinetic models by Friedman, Flynn-Wall-Ozawa, and Kissinger are applicable to waste PWB pyrolysis at temperatures below 400 °C. Moreover, CaO, CaCO3, Fe2O3, Y-Zeolite, and ZSM-5 show a potential to reduce the amount of HBr gas evolved during pyrolysis in TG-DTA-MS. However, in the tube furnace pyrolysis experiments, CaO and CaCO3 were found to be the most effective chemical additions, with more than 90% reduction in total bromine (HBr and other brominated gases) evolved.;It has also been demonstrated that the sequential leaching of waste PWBs with hydrochloric acid, nitric acid and aqua regia is capable of selective recovery of base and precious metals contained in waste PWBs. |