| With the rapid increase in areal density in longitudinal magnetic recording, it is widely believed that the superparamagnetic limit will soon be reached. Perpendicular magnetic recording is now being seriously considered to be a candidate for the replacement. Co/Pd and Co/Pt multilayers are promising candidates because of their high anisotropy, high coercivity, high remanent squareness, and high negative nucleation field. However, Co/Pd and Co/Pt multilayers usually require thick seed layers to promote perpendicular anisotropies, which leads to large “spacing loss”. In this work, different seed layers were studied and it showed that an amorphous indium tin oxide (ITO) seed layer as thin as 2nm could promote good perpendicular anisotropy. The processing parameters for Co-based multilayers such as deposition pressure, temperature, individual layer thickness, and number of bilayers were optimized to obtain better interfaces, higher coercivity, and higher anisotropies.; Boron was added as dopants into Co layers to obtain better intergranular segregation and reduce the grain growth during the thin film deposition. The substrates were heated to promote the migration of boron atoms. It was proved that the addition of boron has successfully reduced the magnetic domain sizes as well as the media noise. Spin stand test showed that the CoB/Pd multilayers with 2nm ITO seed layer and 6μm thick NiFe soft underlayers deposited at 230°C gave a D50 of 340 kfci for differentiated output signals and an areal density of 11 Gb/in2 at a bit-error-rate of 10 −7. Given narrower heads, better soft underlayer, and lower flying height, the media can reach a much higher recording density. |