Processing, Microstructure, and Mechanical Properties of Interpenetrating Biomorphic Graphite/Copper Composites

Composite properties can surpass those of the individual phases, allowing for the development of advanced, high-performance materials. Bio-inspired and naturally-derived materials have garnered attention as composite constituents due to their inherently efficient and complex structures. Wood-derived ceramics, produced by converting a wood precursor into a ceramic scaffold, can exhibit a wide range of microstructures depending on the wood species, including porosity, pore size and distribution, and connectivity.;The focus of this work was to investigate the processing, microstructure, and properties of graphite/copper composites produced using wood-derived graphite scaffolds. Graphite/copper composites combine low specific gravity, high thermal conductivity, and tailorable thermal expansion properties, and due to the non-wetting behavior of copper to graphite, offer a unique system in which mechanically bonded interfaces in composites can be studied. Graphite scaffolds were produced from red oak, beech, and pine precursors using a catalytic pyrolyzation method, resulting in varying types of pore networks. Two infiltration methods were investigated to overcome challenges associated with non-wetting systems: copper electrodeposition and pressure-assisted melt infiltration.;The phase distributions, constituent properties, interfacial characteristics, mechanical behavior, and load partitioning of these biomorphic graphite/copper composites were investigated, and were correlated to the wood species. The multi-domain feature sizes in the graphite scaffolds resulted in composites with copper relegated not only to the large, connected channels produced from the transport features in the wood, but also within the smaller, lower aspect ratio fibrous regions of the scaffold. Both features contributed to the mechanical behavior of the composites to varying degrees depending on the wood species.;A multi-component predictive model also was developed and used to guide the additive-assisted electroplating of the graphitized scaffold, and helped illuminate the roles of plating additives in macro-sized channels. The model can be adapted for many material systems, sample geometries, and plating conditions to investigate the use of metal electrodeposition as a means of scaffold infiltration. Additionally, X-ray diffraction tomography was used to resolve position-dependent strain in a composite. The results of this nascent capability were discussed with respect to a two-component system under increasing uniaxial load, and compared to the results of conventional volume-averaged measurements.