CORROSION IN MAGNESIUM AND A MAGNESIUM ALLOY (AZ91C) AS MODIFIED BY ION IMPLANTATION (POLARIZATION CURVE, ANGER, IRON IMPLANTATION, BORON, SCANNING ELECTRON MICROSCOPE)

Magnesium and a magnesium alloy (AZ91C) have been ion implanted over a range of ions energies (50 to 150 keV) and doses (1 x 10('16) to 2 x 10('17) ions/cm('2)) to modify the corrosion properties of the metals. The corrosion tests were done by anodic polarization in chloride-free and chloride-containing aqueous solutions of a borated-boric acid with a pH of 9.3. Anodic polarization measurements showed that some implantations could greatly reduce the corrosion current densities at all impressed voltages and also increased slightly the pitting potential, which indicated the onset of the chloride attack. These improvements in corrosion resistance were caused by boron implantations into both types of samples. However, iron implantations were found to improve only the magnesium alloy.; To study the corrosion in more detail, Scanning Auger Microprobe Spectrometer (SAM), Scanning Electron Microscope (SEM) with an X-ray Energy Spectrometry (XES) attachment, and Transmission Electron Microscope (TEM) measurements were used to analyze samples before, after, and at various corrosion stages.; In both the unimplanted pure magnesium and AZ91C samples, anodic polarization results revealed that there were three active corrosion stages (Stages A, C, and E) and two passivating stages (Stages B and D). Examination of Stages A and B in both types of samples showed that only a mild, generalized corrosion had occurred. In Stage C of the TD samples, a pitting breakdown in the initial oxide film was observed. In Stage C of the AZ91C samples, galvanic and intergranular attack around the Mg(,17)Al(,12) intermetallic islands and along the matrix grain boundaries was observed. Stage D of both samples showed the formation of a thick, passivating oxygen containing, probably Mg(OH)(,2) film. In Stage E, this film was broken down by pits, which formed due to the presence of the chloride ions in both types of samples.; Stages A through D of the unimplanted samples were not seen in the boron or iron implanted samples. Instead one low current density passivating stage was formed, which was ultimately broken down by the chloride attack. It is believed that the implantation of boron modified the initial surface film to inhibit corrosion, whereas the iron implantation modified the intermetallic (Mg(,17)Al(,12)) islands to act as sacrificial anodes.