The environmental applications and implications of nanotechnology in membrane-based separations for water treatment

This dissertation presents results of three related projects focused on the applications of membrane separation technology to water treatment: 1) Experimental design and evaluation of polyelectrolyte multilayer films as regenerable membrane coatings with controllable surface properties; 2) Modeling of the interactions of nanoscale TiO2 and NOM molecules in aqueous solutions of environmentally relevant compositions; 3) Experimental design and preliminary testing of a membrane-based crossflow filtration hydrocyclone process for the separation of oil-in-water dispersions.;Chapter 2 describes the design of polyelectrolyte multilayers as nanoscale membrane coatings and their application in nanofiltration of feed waters that contain suspended colloids and dissolved species. Layer-by-layer deposition of anionic and cationic polyelectrolytes was employed to prepare membrane coatings allowing for a fine control over their surface properties. This approach to membrane design also affords a possibility of regenerating coatings after they are fouled by colloids. This project demonstrated, for first time, the possibility of designing nanofiltration membranes with regenerable skin.;Chapter 3 describes a study on the mechanisms of natural organic matter (NOM) adsorption onto the surface of titania nanoparticles. Titainia (TiO 2) is often used in the fabrication of ceramic membranes and understanding how NOM interacts with TiO2 can help to better predict ceramic membrane fouling by NOM-containing waters. The combined effect of pH and calcium on the interactions of nonozonated and ozonated NOM with nanoscale TiO 2 was investigated by applying extended Derjaguin --- Landau --- Verwey - Overbeek (XDLVO) modeling. XDLVO surface energy analysis predicted NOM adsorption onto TiO2 in the ozone-controlled regime but not in the calcium-controlled regime. In both regimes, short range NOM-NOM and NOM-TiO2 interactions were governed by acid-base and van der Waals forces, whereas the role of electrostatic forces was found to be relatively insignificant. Ozonation increased the surface energy of NOM, contributing to the hydrophilic repulsion component of the NOM-NOM and NOM-TiO2 interactions. In the calcium-controlled regime, non-XDLVO interactions such as intermolecular bridging by calcium were hypothesized to be responsible for the observed adsorption behavior.;Chapter 4 describes research on the crossflow filtration hydrocyclone separation of oil-in-water dispersions wherein a ceramic tubular membrane was used as the permeable wall of the hydrocyclone. Air sparging was applied to mitigate oil fouling. A dual membrane system consisting of an outer hydrophilic ceramic membrane and an inner hydrophobic polymeric membrane was evaluated to test the possibility of separating the dispersion into two streams: 1) oil with zero or very low concentration of water and 2) water with zero or very low concentration of oil. The performance of the dual membrane system indicated the possibility of using membranes with different chemical affinities to cost-effectively separate the oil-water dispersion into two separate phases. The incorporation of air sparging to membrane filtration was found to be effective in mitigating oil fouling with improved permeate flux.