| Static corrosion studies were undertaken to determine the compatibility of several candidate high temperature materials for a heat transfer loop in a molten alkali fluoride eutectic salt, LiF-NaF-KF: 46.5-11.5-42 mol % (commonly referred to as FLiNaK), as well as a molten chloride near eutectic salt, KCl-MgCl2: 68-32 mol %. Several high temperature alloys: Hastelloy-N, Hastelloy-X, Haynes-230, Inconel-617, and Incoloy-800H, Nb-1Zr, a nearly pure Ni alloy Ni-201, and a C/SiSiC ceramic were exposed to molten FLiNaK at 850°C for 500 h in sealed graphite crucibles under an argon cover gas. Corrosion occurred predominantly from dealloying of Cr from the Cr bearing alloys, an effect that was particularly pronounced at the grain boundaries. Corrosion was noted to occur from selective attack of the Si phase in the C/SiSiC ceramic. Alloy weight-loss/area due to molten fluoride salt exposure correlated with the initial Cr-content of the alloys, and was consistent with the Cr-content measured in the salts after corrosion tests. The alloys' weight-loss/area was also found to correlate to the concentration of carbon present in the nominally 20% Cr containing alloys, due to the formation of chromium carbide phases at the grain boundaries. The corrosion mechanisms for the chloride based salt were found to be similar to those observed in FLiNaK, but the chemical attack was found to be less aggressive.;Sulfamate Ni electroplating and Mo plasma spraying of Fe-Ni-Cr alloy coupons was investigated to mitigate Cr dissolution. A chemical vapor deposited pyrolytic carbon and SiC coating was also investigated to protect the C/SiSiC composites. Results indicate that Ni-plating has the potential to provide protection against alloy corrosion in molten fluoride salts. Furthermore, the presence of a chromium-oxide interlayer at the interface of the Ni-plating and alloy substrate can further improve the efficacy of the Ni-plating. The pyrolytic carbon and SiC coating on the C/SiSiC composites was effective in eliminating the attack of the Si phase in the composites. Delamination of the Mo coating in FLiNaK prevented further investigation of this promising approach. |