| Al-Mg alloys are well suited for marine applications due to their low density, ease of fabrication, structural durability, and most notably resistance to corrosion. The purpose of this study is to investigate the effects of alloying additions, mechanical processing and heat treatments on the development of grain boundary phases that have an effect on intergranular corrosion (IGC).;Cu, Zn, and Si modified compositions of AA5083 were produced that were subjected to a low and high degree of cold work and various heat treatments. ASTM G67 (NAMLT) intergranular corrosion testing and detailed microstructural characterization for various alloys was carried out. An optimal composition and processing condition that yielded the best intergranular corrosion resistant material was identified based on the ASTM G67 test screening.;Further, the outstanding modified AA5083 was selected for further microstructural analysis. This particular alloy with has a magnesium level high enough to make it susceptible to intergranular corrosion is very resistant to IGC. It was found that development of the appropriate sub-structure with some Cu, Si and Zn resulted in a material very resistant to IGC. Formation of many sinks, provided by sub-boundaries, within microstructure is very beneficial since it produces a relatively uniform distribution of Mg in the grain interiors, and this can suppress sensitization of this alloy very successfully. This is a very promising rote for the production of high-strength, and corrosion resistant aluminum alloys.;Additionally in this study, TEM sample preparation become very crucial step in grain boundary phase investigation. Focus Ion Beam (FIB) milling was used as a primary TEM sample preparation technique because it enables to extract the samples from desired and very specific locations without dissolving grain boundary phases as it was in conventional electropolishing method. However, other issues specifically relevant to FIB milling of aluminum alloys related to Ga accumulation were discovered, that produce significant microstructural artifacts. It is well known that liquid gallium can cause Liquid Metal Embitterment (LME) aluminum alloys, and gallium readily penetrates aluminum grain boundaries. Low energy Ar ion nanomilling is potentially quite effective at removing gallium from the external and internal surfaces of aluminum thin foils, but can still leave persistent artifacts. Al-Mg alloys can be also susceptible to localized corrosion such as pitting corrosion in the presence of chloride ions. In this study the phases responsible for this type of corrosion were identified. ASSET (ASTM G66) test was used to determine the influence of heat-treatment on pitting corrosion on various modified AA5083 alloys. Additionally, potentiodynamic polarization as well as potentiostatic measurements in conjunction with SEM analysis were carried out to obtain pitting potential (Epit) and to determine the location of metastable pit initiation, respectively. |