Fabrication of nanostructures and nanostructure based interfaces for biosensor application

Nanoparticles have applications from electronics, composites, drug-delivery, imaging and sensors etc. Fabricating and controlling shape and size of nanoparticles and also controlling the positioning of these particles in 1, 2 or 3-d structures is of most interest. The underlying theme of this study is to develop simple and efficient techniques to fabricate nanoparticles from polymers, and also achieve control in shape, size and functionalization of nanoparticles, while applying them in biosensor applications. First part of the dissertation studies the fabrication of nanostructures using anodized alumina membrane as template. It discusses the fabrication design for injecting polystyrene nanoparticles inside the pores of anodized alumina membranes and heating the membrane to coalesce the particles into tapered nanoparticles. Various parameters like temperature and amount of injected particles can vary the size and shape of fabricated nanoparticles. Later it focuses on the fabrication of metallic nanostructures using the alumina membranes without the aid of the injection system. It utilizes the difference in the functionality of the pore edges of cleaved alumina membrane with respect to the pore walls to first deposit charged polymers using layer-by-layer deposition followed by deposition of nickel. Second part of this study involves immobilization of enzymes for biosensor applications. It describes a biosensor interface developed by immobilization of tyrosinase using layer-by-layer (LBL) deposition process. The interface was modified with functional nanoparticles and their influence on the response of biosensor was studied. Tyrosinase sensor was further extended to develop a novel biosensor which was used to study real time inhibition of NEST, a subunit of the medically relevant membrane protein, neuropathy target esterase. The biosensor was developed to give real time monitoring of dose dependent decrease in activity of NEST. Final part of this study emphasizes on the influence of high shear rate mixer from PRIMIX, Japan on polymer particle formation. This mixer can process specific volume of liquid and subject it to high shear conditions. The mixing geometry consists of concentric cylinders, 52 mm inner turbine diameter and 58 mm vessel diameter, with inner turbine rotating at high peripheral speeds ranging from 10 m/s to 50m/s. The mixing is in turbulent regime at all the speeds. Poly-lactic acid (PLA) nanoparticles were fabricated by nanoprecipitation and emulsion diffusion process. Nanoprecipitation process was independent of shear rate at low mixing speeds and particle size went up at high speeds due to coalescence of PLA particles. Emulsion diffusion was done by making oil in water emulsion. PLA dissolved in ethyl acetate was used as oil phase. It was followed by diffusion of ethyl acetate in excess amount of DI water. It followed expected trend of smaller size at high mixing speeds but was very sensitive to mixing time where particles coalesced at longer time duration. The influence of viscosity was also studied and particles changed shape from spherical nanoparticles to micron sized open shells at high viscosity and high mixing speeds due to heating combined with mixing occurring in viscous turbulent regime.