Electrochemical corrosion and modeling studies of types 7075 and 2219 aluminum alloys in a nitric acid + ferric sulfate deoxidizer solution

The corrosion behavior of types 7075-T73 and 2219-T852 high strength aluminum alloys have been investigated in a HNO3 + Fe2(SO 4)3 solution. The materials are characterized in the time domain using the electrochemical noise resistance parameter (Rn) and in the frequency-domain using the spectral noise impedance parameter ( Rsn). The Rsn parameter is derived from an equivalent electrical circuit model that represents the corrosion test cell schematic used in the present study. These calculated parameters are correlated to each other, and to corresponding scanning electron microscopy (SEM) examinations of the corroded surfaces. In addition, energy dispersive spectroscopy (EDS) spectra are used in conjunction with SEM exams for particle mapping and identification. These constituent particles are characterized with respect to their size and composition and their effect on the localized corrosion mechanisms taking place. Pitting mechanisms are identified as 'circumferential' where the particles appeared noble with respect to the aluminum matrix and by 'selective dissolution' where they are anodic to the aluminum matrix. The electrochemical data are found to be in good agreement with the surface examinations. Specifically, the electrochemical parameters Rn and Rsn were consistent in predicting the corrosion resistance of 7075-T73 to be lower than for the 2219-T852 alloy. Other characteristic features used in understanding the corrosion mechanisms include the open circuit potential (OCP) and coupling-current time records.