Intermediate temperature grain boundary embrittlement in nickel-base weld metals

The ductility-dip cracking (DDC) susceptibility of NiCrFe filler metals was evaluated using the strain-to-fracture (STF) GleebleRTM-based testing technique1. These high chromium Ni-base filler metals are frequently used in nuclear power plant applications for welding Ni-base Alloy 690 and included INCONELRTM Filler Metal 52 and 52M (FM-52 and FM-52M)2, and a number of FM-52M-type experimental alloys including two with additions of molybdenum and niobium. A wide range in DDC susceptibilities was observed in the tested alloys including significant variations in susceptibility with only small compositional changes. The interpretation of the STF results now includes both the threshold strain for cracking and the transition to "massive" cracking. While the threshold strain is still insightful and an indication of cracking susceptibility, materials which transition rapidly from the threshold strain to "massive" cracking are typically more susceptible to DDC.; The spot pre-welds made on the STF samples, used to produce a repeatable microstructure were found to significantly affect the DDC resistance when the current downslope time was altered. Decreasing the downslope time resulted in a faster cooling rate, finer solidification substructure, fewer metastable intragranular precipitates, and a reduced DDC susceptibility. The downslope time has been found to be the most important STF testing variable evaluated to date.; A significant decrease in DDC susceptibility was observed in the alloys with Mo and Nb additions. The threshold strain for cracking in the 2.5% Nb and 4% Mo NiCrFe alloy was approximately 10%, and demonstrated a DDC resistance of more than twice that observed in typical FM-82 alloys. This remarkable increase in DDC resistance was attributed to the skeletal precipitate morphology whose large surface area and dense distribution were highly effective at pinning grain boundaries and preventing crack initiation. The resulting wavy or tortuous grain boundaries act to mechanically lock the grains together and thereby reduce the cracking susceptibility.; A general improvement in the DDC cracking resistance of FM-52M-type alloys was observed over FM-52, particularly at lower temperatures (750°C) in the DDC range. Compositional changes in the FM-52M experimental alloys resulted in a range of DDC susceptibilities, indicating the strong effect of minor changes in composition. Boron additions resulted in an increase in Cr-rich M23C6 intergranular carbides in the as-welded condition. Electron backscatter diffraction (EBSD) data showed increased intragranular deformation that was attributed to improved grain boundary strengthening as a result of the intergranular M23C6 formation prior to deformation. Elongated intergranular carbides were also found to be more effective in improving grain boundary strengthening when compared with more symmetrical carbides. (Abstract shortened by UMI.); 1GleebleRTM is a registered trademark of Dynamic Systems Inc. 2INCONELRTM is a registered trademark of Special Metals Company, a PCC company.