Cermet anodes for solid oxide fuel cells (SOFC) systems operating in multiple fuel environments: Effects of sulfur and carbon composition as well as microstructure

A series of cermet powders of composition NixCo(1-x) O-YSZ were synthesized for testing as cermet anode materials for SOFCs. The Co is found by powder XRD to become incorporated into the crystal lattice of the NiO, thus forming a true alloyed material. SEM and EDS results show two types of particles upon sintering to 1380oC: small, amorphous particles of YSZ and large, crystalline particles of nickel.;Following reduction in pure hydrogen, the fuel was changed to a mixture with high concentration of H2S. It was found that a concentration of 10 % H2S/H2 produced a sudden change in anode microstructure and resulted in loss of exchange current density. Lowering the amount of H2S in the initial fuel feed, which allowed for a more gradual microstructural change, allowed the cell to eventually function at concentrations in excess of 10 % H2S/H2. It was determined by OCV values in various concentrations of H2S/H2 that hydrogen is the predominant fuel of choice, even if H2S is available. Following electrochemical testing, slow cooling in a 10 % H2S/H2 mixture following produced metal sulfide spheres, as determined by SEM and EDS.;Investigation in hydrocarbon, alcohol and biodiesel fuels was then undertaken to test the fuel variability of the given cermet anode material. Methane containing 10 % H2S was found to have increased exchange current density relative to poisoned hydrogen. Ethane and biodiesel experienced no increase in exchange current density, but a lengthening of the functional lifetime of the cell was observed, indicating reduced carbon poisoning. Methanol is a promising oxygen-containing SOFC fuel since it produced exchange current density values larger than hydrogen, and showed no evidence of coke formation by post-mortem SEM.;Since oxygen-containing fuels are known to decompose in the gas phase at typical SOFC operating temperatures, the performance in a mixture of various CO/H2 fuels was then investigated. The Ni0.7Co 0.3O-YSZ cermet anode gave higher exchange current density values for low ratio of CO/H2 fuels in the range 20/80 and 30/70 compared to pure H2. This is the first example of a Ni-based anode providing higher performance with a CO/H2 mixed fuel than for a pure H 2 fuel. Finally, continuous running of a cell with fuel ratio 25/75 CO/H2 for 7 days produced exchange current density values, which were observed to increase significantly above the values for pure H2 during days 1-4 followed by deterioration below the value for hydrogen on subsequent days.;The electrochemical oxidation of hydrogen on a cermet anode composed of Ni0.7Co0.3O-YSZ was investigated using a series of many button cells. Through EIS data, cyclic voltammetry data, the exchange current densities for these button cells were determined. Although a relatively large variation was found (expected to be due to microstructural variation) the average values for both methods of measurement is in good agreement in hydrogen.