An experimental and computational investigation of dynamic ductile fracture in stainless steel welds

The high strain rate viscoplastic flow and fracture behavior of NITRONIC-50 and AL6XN stainless steel weldments are studied under dynamic loading conditions. The study is primarily motivated by interest in modeling the micromechanics of dynamic ductile failure in heterogeneous weldments. The high strain rate response of specimens machined from the parent, weld and heat-affected zones of NITRONIC-50 and AL6XN weldments is reported here on the basis of experiments conducted in a compression Kolsky bar configuration. The failure response of specimens prepared from the various material zones is investigated under high rate loading conditions in a tension Kolsky bar set-up. The microstructure of voided fracture process zones in these weldments is studied using X-ray Computed Microtomography. To model the preferential evolution of damage near the heat-affected zone, a finite deformation elastic-viscoplastic constitutive model for porous materials is developed. The evolution of the macroscopic flow response and the porous microstructure have been analysed in two distinctive regimes: pre-coalescence and post-coalescence. The onset of void coalescence is analyzed on the basis of upper-bound models to obtain the limit-loads needed to sustain a localized mode of plastic flow in the inter-void ligament. A finite element framework for the integration of the porous material response under high rate loading conditions is implemented as a user-subroutine in ABAQUS/Explicit. To address the effect of mesh sensitivity of numerical simulations of ductile fracture, a microstructural length scale is used to discretize finite element models of test specimens. Results from a detailed finite element study of the deformation and damage evolution in AL6XN weldments are compared with experimental observations.