Plasma -assisted MBE growth kinetics and characterization studies of wide bandgap III-V epitaxial materials

Scope and method of study. The purpose of this research was to understand the physics of RF plasma-assisted molecular beam epitaxial growth of GaN epitaxial films and InGaN/GaN superlattice structures grown on Al2O3 (0001) substrates. The techniques used to characterize the RF-MBE grown samples include in situ reflection high energy electron diffraction (RHEED) and optical pyrometry, and ex situ spatially-resolved high resolution X-ray diffraction, spatially-resolved reflectance spectroscopy, atomic force microscopy, and low-temperature photoluminescence (PL) spectroscopy.;Findings and conclusions. RF plasma-assisted molecular beam epitaxy (RF-MBE) has been used to grow GaN epitaxial films and InGaN/GaN superlattice structures. The most important growth parameters in the growth of GaN epitaxial films were identified as the substrate temperature, incident N*/Ga flux ratio, and GaN growth rate. The effect of these growth parameters on GaN growth and quality of GaN epitaxial films is discussed. Additionally, an interpretation of the effects of growth conditions on the underlying microscopic growth processes occurring is presented. All of the observed GaN growth results may be understood in terms of these microscopic growth processes. InGaN/GaN superlattice samples are grown to identify and quantitatively access the InGaN growth phenomenology. It is inferred that InN requires a higher N*/III flux ratio than does GaN for stoichiometric growth. At substrate temperatures below 590°C, the In composition of the superlattice samples is nominally constant. However, in the narrow temperature range 590--670°C, the In composition decreases by more than an order-or-magnitude at the lowest N*/III flux ratio of this study. Additionally, the incident N*/III flux ratio is found to strongly influence the In composition as well. Nearly an order-of-magnitude increase in In composition is observed despite only a 20% increase in the N*/III flux ratio at the highest temperature of this study. RHEED and PL measurements support the assessment of the In reduction mechanism as thermally-activated surface-segregation and surface-desorption of In. Implications of these results for device growth are discussed.