Antibacterial Properties Of Nano-silver Coated PEEK Prepared Through Magnetron Sputtering

Objective:In this study,polyetheretherketone(PEEK)implant material was modified by low temperature magnetron sputtering technique to obtain nano-silver layer on the surface of PEEK.The cytotoxicity and antibacterial properties of PEEK were investigated through a series of in vitro tests and provide a theoretical basis for its use in clinical applications.Methods:The surfaces of PEEKs were coated with nano-silver at varying thicknesses(3,6,9,and 12 nm)through magnetron sputtering technology.The resulting coated PEEK samples were classified into the following groups according to the thickness of the nano-silver coating: PEEK-3(3nm),PEEK-6(6 nm),PEEK-9(9 nm),PEEK-12(12 nm),and PEEK control group.The surface microstructure and composition of each sample were observed by scanning electron microscopy(SEM),atomic force microscopy(AFM),and energy dispersive spectrum(EDS)analysis.The water contact angle of each sample was then measured by contact angle meters.A cell counting kit(CCK-8)was used to analyze the cytotoxicity of the mouse fibroblast cells(L929)in the coated groups(n=5)and group test samples(n=6),negative control(polyethylene,PE)(n=6),and positive control group(phenol)(n=6).The antibacterialproperties of the samples were tested by co-culturing Streptococcus mutans and Straphylococcus aureus.The bacteria that adhered to the surface of samples were observed by SEM.The antibacterial adhesion ability of each sample was then evaluated.Results:SEM and AFM analysis results showed that the surfaces of control group samples were smooth but compact.Homogeneous silver nano-particles(Ag NPs)and nano-silver coating were uniformly distributed on the surface of the coated group samples.Compared with the control samples,the nano-silver coated samples had a significant increase in surface roughness(P < 0.05)as the thickness of their nano-silver coating increased.EDS analysis showed that not only C and O but also Ag were present on the surface of the coated samples.Moreover,the water contact angle of modified samples significantly increased after nano-silver coating modification(P < 0.01).CCK-8cytotoxicity test results showed that coated samples did not exhibit cytotoxicity.The antibacterial experimental results showed that the nano-silver coating can significantly improve the antibacterial activity and bacterial adhesion ability of the PEEK samples.Conclusions:The compact and homogeneous nano-silver coating was successfully prepared on the surface of PEEK through magnetron sputtering.The nano-silver coated PEEKs demonstrated enhanced antibacterial activities and bacterial adhesion abilities and had no cytotoxic effects.