Solid-state NMR studies of polymer adsorption onto metal oxide surfaces

This dissertation presents solid-state NMR studies that probe the dynamic and conformational properties of polymers adsorbed on solid surfaces in the dry state. The systems studied include a series of ethylene based random copolymers where the binding group is modified, and two diblock copolymer systems where the blocks have different intrinsic mobilities and surface interactions. The thesis begins by looking at the structures formed by the adsorption of poly (ethylene-co-acrylic acid) (PEA), poly (ethylene- co-vinyl alcohol) (EVOH), poly (ethylene-co-vinyl acetate) (EVA), and polyethylene (PE) on metal oxide powders (zirconia and alumina). NMR spectroscopy, FTIR-PAS, and TGA were used to characterize the surface behaviour of the systems with comparisons made between the bulk and adsorbed copolymers. 13C CPMAS, 1H and T 1 relaxation measurements were all recorded with the aim of correlating the microscopic structure of the surface with changes in NMR data. The chain conformation of adsorbed ethylene copolymers was found to strongly depend on the binding strength of the polar sticker groups with the substrates.;The diblock copolymers poly (2-vinylpyridine), poly (isoprene)- b-poly (2--vinylpyridine), (PI-P2VP) and poly (isoprene)- b-poly (4-vinylpyridine) (PI-P4VP) were selected to complement the PS-PAA system as both systems have been studied by surface force microscopy. The large contrast in chain mobilities of the PI and PVP blocks allowed spectral editing through variation of the 13C cross polarization parameters. The trends in mobility with block size differ from that of PS-PAA in that the segmental mobility of the buoys increases with anchor block size as expected. The chain mobility of the collapsed PI brushes is significantly enhanced as compared to the bulk state, again supporting the interpretation of surface microscopy studies which require an entropically unfavorable flattened, yet rubbery, surface structure.;The chain dynamics of adsorbed diblock copolymers in the dry state are reported for the first time. Poly (styrene)-b-poly ( t-butyl acrylate) (PS-PtButA) and poly (styrene)-b-poly (acrylic acid) (PS-PAA) were selected to vary both the block size and the binding strength. Once again the primary surface characterization methods are NMR spectroscopy, FTIR-PAS, and TGA. 13C CPMAS, 1H, T1, and T1rho relaxation measurements were all recorded with the aim of correlating the surface structures with changes in NMR data. For the most part, the observed trends in the chain mobilities of the anchor (PAA) and buoy (PS) blocks with block size can be correlated with the predicted mushroom, intermediate and extended brush structures which collapse upon removal of the solvent. However, the chain mobility of the PS buoys decreases with increasing anchor block size. Although the chain mobility of the PS buoys are moderately enhanced relative to the bulk state, the mobility is sufficiently restricted to comfirm the picture of a thin glassy layer with adhesive properties similar to the surface of bulk polystyrene.