| Polymeric surfaces and films have very broad applications in industry. They have been employed as anticorrosive, abrasive and decorative coatings for many years. More recently, the applications of functional polymer films in microelectronics, optics, nanocomposites, DNA microarrays, and enzyme immobilizations has drawn a lot of attention. There are a number of challenges associated with the implementation of functional polymeric surfaces, and these challenges are especially important in the field of surface modification. In this thesis, three different challenges in the field of polymeric functional surfaces are addressed: first of all, a set of rules for the molecular design are presented in chapters 3 and 4 according to the surface needs. Second, some latent energy source must be incorporated into the material design to quantitative modify a surface. Third, the morphology of the surface, the method use to fabricate the design surface and their new applications are presented in chapters 4 and 5.The new polymeric surface functionalization method described in Chapter 3 is based upon an end-functionalized diblock copolymer design to self-assemble at the surface of both hard and soft surfaces. It is demonstrated that alkyne end-functional diblock copolymers can be used to provide precise control over areal densities of reactive functionality. The areal density of alkyne functional groups is precisely controlled by adjusting the thickness of the block copolymer monolayer, which is accomplished by changing either the spin coating conditions (i.e., rotational speed and solution concentration) or the copolymer molecular weight. The modified surfaces are characterized by atomic force microscopy (AFM), contact angle, ellipsometry, fluorescent imaging and angle-dependent X-ray photoelectron spectroscopy (ADXPS) measurements.In Chapter 4, a simple means is demonstrated to covalently bond DNA to polymer-modified substrates the method provides quantitative control of the DNA areal density. The approach is based upon synthesis of an alkyne-end-functional diblock copolymer alpha-alkyne-o-Br-poly(tBA- b-MMA). The block copolymer self-assembles to form a bilayer on the substrate and directs alkyne groups to the surface. Azido-functionalized DNA is immobilized on alkyne functionalized substrates by a "click" reaction. The density of immobilized DNA can be quantitatively controlled by varying the parameters used for spin-coating the polymer film or by adjusting the hydrophilicity of the polymer surface underlying the reactive alkyne functional groups.In Chapter 5, Layer by layer (LbL) assembly techniques construct multilayer thin films by sequential deposition of monomolecular layers of organic molecules. One of the drawbacks associated with their use is that monomolecular layers are usually held together by relatively weak forces such as Van der Waals, electrostatic and hydrogen bonding interactions, and can therefore be lacking in mechanical integrity. In this chapter, it is demonstrated that heterobifunctional polymers, functionalized with one azide chain terminus and a protected alkyne group as the other chain terminus, constitute a powerful and versatile means for the covalent layer-by-layer (CLbL) assembly of thin polymer films. Each monomolecular polymer layer is covalently bound to both the preceding and following layers to produce a robust multilayer structure. Because the coupling chemistry used, "click" chemistry, is highly chemoselective, the layering process is virtually independent of the chemical nature of the polymer so that the constitution of each layer can be selected at will. Unlike other layer-by-layer deposition techniques, the layer thickness in CLbL is not equivalent to the diameter of the polymer chain, but is related to the polymer chain length and can be controlled by adjustment of either the polymer molecular weight or the areal density of surface alkyne groups. |
