Tailoring metal/metal oxide nanostructures for ultra-sensitive detection

This thesis presents three diverse approaches to harnessing the material properties of nanostructures to produce ultra-sensitive detection platforms. In this work we have utilized nanostructure synthesis as the launching point for the creation of nanodevices with applications in chemical and biological sensing, catalysis and metrology.;Silver nanowires were electrodeposited into a porous aluminum oxide (PAO) template. When these templates are chemically etched the nanowires become exposed and eventually collapse into bundles that harbor interstices that function as "hot-spots" for Raman field enhancement. Surface enhanced Raman spectroscopy experiments were carried out on these substrates in two ways using benzenethiol as the Raman probe. In both experiments the SERS spectra show significant (~25 and ~50 fold respectively) increase in intensity over the initial value (when the tips were barely exposed).;Nanostructured titania (NST) thin films were produced by oxidizing titanium with hydrogen peroxide. These films are particularly well suited for integration into microfabricated sensing devices. The formation of NST relies on a re-deposition process in which an adequate amount of Ti-peroxo species must be generated and remain at the solid-solution interface. To reliably produce arrays of micro-patterned NST films on the wafer scale a patterning guide was developed and tested.;Wafer scale arrays of NST micro gas-sensors have been fabricated using standard thin film techniques. Sensing elements are 20 mum on a side. High sensitivity to hydrogen is achieved by modification of the sensors with platinum nanoparticles. When exposed to 10 mT of hydrogen at 250°C, the functionalized devices exhibit more than one order of magnitude decrease in resistance with a response time of ~7 seconds.;Both NST and tin (IV) oxide nanowires were coated in aminosilane self-assembled monolayers (SAMs) which have many applications in binding biomolecules. There has been a plethora of characterization techniques developed for SAMs but unluckily most of them rely on the SAM being on a planar surface. By "tailoring" our aminosilane SAM modified NSMO surfaces with borohydride reduced silver nanoparticles (AgNP) we are able to reliably image the SAMs using scanning electron microscopy (SEM). These AgNP modified SAMs may have many applications in catalysis, sensing and SERS.