| The need for improved electrochemical storage devices has necessitated research on new and advanced electrode materials. One-dimensional nanomaterials such as nanowires, nanotubes, and nanoribbons, can provide a unique opportunity to engineer electrochemical devices to have improved electronic and ionic conductivity as well as electrochemical and structural transformations.Silicon and germanium nanowires (NWs) were studied as negative electrode materials for lithiumion batteries because of their ability to alloy with large amounts of lithium, leading to 4-10 times higher specific capacities than the graphite standard. These nanowires could be grown vertically off of metallic current collector substrates using the gold-catalyzed vapor-liquid-solid synthesis. Electrochemical measurements of the SiNWs showed that capacities greater than 3,500 mAh/g could be obtained for tens of cycles, while hundreds of cycles could be obtained at lower capacities. As opposed to bulk Si, the SiNWs were observed to maintain their morphology during cycling and did not pulverize due to the large volume changes. Detailed TEM and XRD characterization showed that the SiNWs became amorphous during the first lithiation (charge) and formed a two-phase region between crystalline Si and amorphous Li xSi. Afterwards, the SiNWs remained amorphous and subsequent reaction was through a single-phase cycling of amorphous Si. The good cycling behavior compared to bulk and micron-sized Si particles was attributed to the nanowire morphology and electrode design. The surface chemistry and solid-electrolyte interphase (SEI) were studied using XPS as a function of charge and discharge potential. The common reduction productions expected in the electrolyte (1 M LiPF6 in 1:1 EC/DEC) were observed, with the main component being Li2CO3. The morphology of the SEI was found to change at different potentials, indicating a dynamic process involving deposition, dissolution, and re-deposition on the SiNWs. Longterm cycling performance of the SiNWs in different electrolytes, with various surface modifications and coatings, and other experimental parameters were evaluated.The electrochemical reaction of GeNWs with lithium resulted in capacities of &sim1000 mAh/g for tens of cycles. The GeNWs were also observed to become amorphous after the first charge. Interestingly, very large irreversible capacities were observed in the GeNWs, indicating surface instabilities or reactivity with the electrolyte. To passivate the surface, a thin layer of amorphous Si was used to coat the GeNWs and make Ge-Si coreshell nanowires. This passivation helped to reduce the irreversibly capacity loss and gave reversible capacities typical for the GeNWs.Two positive electrode materials for Li-ion batteries were synthesized in nano-morphologies and characterized. Transformation of layered structured V2O5 nanoribbons into the fully lithiated o-Li 3V2O5 phase was found to depend not only on the width but also the thickness of the nanoribbons. For the first time, complete delithiation of o-Li3V2O5 back to the single-crystalline, pristine V2O5 nanoribbon was observed, indicating a 30% higher energy density. Nanostructured BiOCl, a conversion material, was also synthesized and characterized for its Li insertion properties.Networks of silver nanowires (AgNWs) and single-walled carbon nanotubes (SWNTs) were explored as highly conducting, high surface area, and printable materials for flexible, light-weight supercapacitors. Use of the solution-processible AgNWs and SWNTs, as well as a polymer electrolyte, facilitated the fabrication of an entirely printable device on plastic substrates. The devices showed promising results for high energy and power density supercapacitors, with energy and power densities reaching 24 Wh/kg and 42 kW/kg for the AgNW/SWNT composite. |
