Solute redistribution and constitutional supercooling effects in vertical Bridgman grown indium gallium antimonide by accelerated crucible rotation technique

The ternary alloy, InxGa1- xSb, is a compound semiconducting material of compositionally tunable bandgap (0.18 - 0.72 eV), making it desirable for use in photovoltaic, photodetector, and other opto-electronic devices in the infra-red regime. In the past, this material has proven to be difficult to synthesize in bulk due to the large phase separation between the constituent binaries. In this work, InxGa1-xSb has been grown in a state-of-the-art, computer-controlled system based on vertical Bridgman technique designed to allow crucible rotation during solidification of the material to reincorporate excess solute and improve material quality. Independent thermocouples allow for in situ monitoring and maintenance of the temperature to 0.2°C precision during crystal growth, reducing compositional inhomogeneities caused by temperature fluctuations.;A series of experiments has been performed to evaluate the effect of accelerated crucible rotation technique (ACRT) on the structural quality and compositional homogeneity of bulk-grown InxGa 1-xSb for a starting melt composition of x = 0.25. A lowering rate of 3 mm/hr has been employed, for an overall cooling rate of 5.1°C/hr, which deliberately exceeds the threshold for constitutional supercooling. Scanning electron microscopy (SEM) has been performed on samples of In0.18Ga0.82Sb revealing a 92% percent reduction in micro-cracking with the application of ACRT when compared to synthesis performed without rotation. Furthermore; electron probe microscopy (EPMA) indicates an order of magnitude improvement in compositional homogeneity in the direction of growth with the use of ACRT.;Micro-cracking and compositional homogeneity throughout cross-sections of InxGa1-xSb material also indicate areas of improved mixing during solidification, which can be compared to existing models of fluid flow exhibited in ACRT. The boule synthesized with ACRT shows a decrease in compositional deviation of 62% in the first-to-freeze areas of the sample, indicating suppression of supercooling in areas identified as Ekman flow regions. Results also demonstrate evidence of "dead-zones" in the ACRT mixing in the extreme center of the material, which confirms computational models of ACRT-induced fluid flow above the Ekman shear layer.