Squeeze casting as alternative fabrication process for carbon fiber reinforced aluminium matrix composites

Aluminium matrix composites are among the most promising candidate materials for light weight and high strength applications such as transportation and armour. In a previous study 6061 aluminum matrix composites reinforced with plain weave carbon fiber preform (AS4 Hexcel) were successfully fabricated by squeeze casting using the laminate fabrication technique. This research aims at optimizing the fabrication process in order to achieve improved strength and mechanical properties. It focuses on the liquid infiltration squeeze casting method. Good mechanical bonding between fiber and aluminium is achieved thanks to improved infiltration and impregnation of the fabric by liquid aluminium. Oxidation products at fiber/aluminium interface and porosity are reduced. As a result, composites are produced with overall improved mechanical properties. The flexural strength is increased by up to 19.9% and 15.4% compared to the laminate approach and the reference 6061 aluminium alloy squeeze cast under identical conditions, respectively. Similarly, overall hardness is improved. However, the impact strength is reduced by 7.76% and 25.78% when compared to casts fabricated by the laminate method and the reference aluminium alloy, respectively. The thesis constitutes a good basis for further research on fiber and particle reinforced aluminium matrix composites with the goal of further improving fracture toughness, particularly for gradient materials used in armour applications.