Effects of silicon, copper and iron on static and dynamic properties of alloy 206 (aluminum-copper) in semi-solids produced by the SEED process

The advantages of producing metal parts by rheocasting are generally recognised for common foundry alloys of Al-Si. However, other more performing alloys in terms of mechanical properties could have a great interest in specialized applications in the automotive industry, while remaining competitive in the forming. Indeed, the growing demand for more competitive products requires the development of new alloys better suited to semi-solid processes. Among others, Al-Cu alloys of the 2XX series are known for their superior mechanical strength. However, in the past, 2XX alloys were never candidates for pressure die casting. The main reason is their propensity to hot tearing. Semi-solid processes provide better conditions for molding with the rheological behavior of dough and molding temperatures lower reducing this type of defect.;In the initial phase, this research has studied factors that reduce hot tearing susceptibility of castings produced by semi-solid SEED of alloy 206. Subsequently, a comparative study on the tensile properties and fatigue was performed on four variants of the alloy 206. The results of tensile strength and fatigue were compared with the specifications for applications in the automotive industry and also to other competing processes and alloys.;During this study, several metallurgical aspects were analyzed. The following main points have been validated: i) the main effects of compositional variations of silicon, iron and copper alloy Al-Cu (206) on the mechanical properties, and ii) certain relationships between the mechanism of hot cracking and the solidification rate in semi-solid.;Parts produced from the semi-solid paste coming from the SEED process combined with modified 206 alloys have been successfully molded and achieved superior mechanical properties than the requirements of the automotive industry. The fatigue properties of the two best modified 206 alloys were higher than those of A357 alloy castings and are close to those of the wrought alloy AA6061.;At present, there is simply no known application for pressure die-cast alloy with 206 (Liquid Die-casting). This is mainly due to the high propensity to hot cracking and limitations facing the part geometry and the subsequent assembly. This study demonstrated that in addition to pieces produced by semi-solid die-casting using large variations in chemical composition, the SEED process allows obtaining spare sound (sound part) and more complex geometry. Moreover, as the semi-solid parts have less porosity, they can also be machined and welded for some applications.;The conclusions of this study demonstrate significant progress in identifying the main issues related to the feasibility of die-casting good parts with high performance using the modified 206 alloy combined with SEED process. This work is therefore a baseline work in the development of new Al-Cu alloys for industries of semi-solid and, at the same time, for the expansion of aluminum for high performance applications in the industry.;N.B. This thesis is part of a research project developed by the NSERC / Rio Tinto Akan Industrial Research Chair in Metallurgy of Innovative Aluminum Transformation (CIMTAL)..