Synthesis and characterization of cathode materials for lithium ion-rechargeable batteries

Lithium intercalation materials are of special interest for cathodes in rechargeable lihium-ion batteries, because they are capable of reversibly intercalating lithium ions without altering the main unit. We developed a novel solution-based route for the synthesis of these lithium intercalates oxides. The first part of this work was devoted to the optimization of chemical solution process parameters in order to correlate their electrochemical properties. It was found that the lattice parameters and the crystallite size increase, whereas the lattice strain decreases with the increase in calcinations temperature. Powders annealed at 700°C for 15 h yielded best electrochemical performance. The electrochemical performance of substituted Li1.2Mn2O 4, Li1.2Mn1.8O4, Li1.2Cr 0.05Mn1.95O4, and Li1.2Cr0.05 Mn1.75O4 spinel electrodes in lithium cell has been studied. The electrochemical data showed that the Li and Cr dopant effect improves the cycleablility of spinel LiMn2O4 electrodes. The second part of this dissertation was devoted to improve the rate capabilities of these cathode materials by growing nano-size cathode particles and also by cation co-doping. Though the discharge capacity of these nano-crystalline cathodes was equivalent to their microcrystalline counterpart, these exhibited capacity fading in the 4V range. Through a combined X-ray diffraction, micro-Raman spectroscopy, and X-ray photoelectron spectroscopy (XPS) analyses, we correlated the observed capacity fading with the onset of Jahn-Teller (J-T) distortion toward the end of the discharge in the cut-off limit between 4.2 and 3.2V. It was postulated that J-T distortion is the dominant fading mechanism of these nano-crystalline cathodes then by increasing the average oxidation state of the Mn ion in a virgin lithium manganate cathode, the onset of such distortion towards the end of the discharge could be delayed, and therefore, the cycleability of these cathodes could be improved. By synthesizing lithium and aluminum ion co-doped lithium manganate particles, we could increase the average oxidation state of Mn ions in the virgin electrodes. Indeed, the cycleability of these co-doped cathodes was dramatically improved which supports our population.; The third part of this thesis was devoted to synthesis and electrochemical properties of layered compounds. Lithium nickel oxides derivatives are promising positive materials for the next generation of lithium-ion batteries. Partial substitution of certain cations for nickel in this family of oxides which satisfies the demanding requirements for rechargeable battery applications. In this part the interest is focused on the effect of simultaneous cobalt as well as aluminum doping was studied to understand their effect on the phase formation behavior and electrochemical properties of solution derived lithium nickel oxide cathode materials for rechargeable batteries. (Abstract shortened by UMI.)...