Surface Chemistry and Precursor Material Effects on the Performance of Pyrolyzed Nanofibers as Anodes for Lithium-ion Batteries

Next-generation lithium-ion batteries to meet consumer demands and new applications require the development of new electrode materials. Electrospinning of polymers is a simple and effective method to create one-dimensional, self-supporting materials, with no inactive components after pyrolysis. Composites of these nanofibers and high-capacity lithium materials have been demonstrated to possess superior reversible capacity than state-of-the-art commercial anodes.;Despite impressive reversible discharge capacities polyacrylonitrile-based composites are not ready for adoption in commercial applications. These materials suffer from irreversible losses of Li to formation on the electrode of the solid electrolyte interphase during the first charge of the cell. This thesis work has taken two approaches to engineer high-performing nanofiber-based electrodes.;First, the chemistry at the interface of the electrode and the electrolyte has been changed by depositing new surfaces. Attempts to create a graphitic fiber surface via plasma enhanced chemical vapor deposition did not result in an improvement of the irreversible losses. However, the experiments did demonstrate the growth of large surface area carbon nanowalls on the pyrolyzed electrospun fibers, creating a material which could serve as a substrate in catalysis or as an electrode for composite ultra-capacitors. Additionally, passivation surfaces were deposited by atomic layer deposition and molecular layer deposition. These new surfaces were employed to reduce the irreversible consumption of lithium by moving the charge transfer reaction to the interface of the carbon and the new material. The removal the lithium from the solvent prior to charge transfer limits the irreversible reduction of solvent by metallic lithium.;Alumina films grown by atomic layer deposition reduced lithium losses to the solid electrolyte interphase by up to 42% for twenty deposition cycles. This large improvement in irreversible capacity resulted in a nearly 50% reduction in reversible lithium storage. Thinner coatings of alumina had a less dramatic effect on both the irreversible capacity losses and the reversible discharge capacity. A coating of ten cycles of alumina at a temperature of 150 °C resulted in a 17% reduction in irreversible capacity with negligible impact on the reversible capacity.;Hybrid aluminum-organic films grown by molecular layer deposition also reduced irreversible lithium losses. The largest reduction was 23% for electrodes coated with 40 cycles of the alucone material. For all thicknesses studied these hybrid films delivered less improvement than the alumina grown by atomic layer deposition, with poor reversible lithium storage capacity available at high charging and discharging currents.;Second, polyacrylonitrile has served as the precursor for electrospun composite electrodes because of its ease of processing and well-known carbonization process. Polyimides represent a family of polymers for which the material properties can be tailored by careful monomer selection. These polymers were used as the non-woven matrix to create materials capable of delivering a larger percentage of their maximum reversible capacities at high currents when compared to polyacrylonitrile-based electrodes. These materials had a more graphitic structure based on Raman spectroscopy, and resulted in lower irreversible capacity losses than polyacrylonitrile-based fibers for fibers based on pyromellitic dianhydride and p-phenylene diamine.