Environmental cracking susceptibility of austenitic stainless steel alloys in acidified seawater

Posted on:1995-07-01

Degree:M.S

Type:Thesis

University:Florida Atlantic University

Candidate:Poulassichidis, Antonios N

Full Text:PDF

GTID:2471390014989879

Subject:Engineering

Abstract/Summary:

The stress corrosion cracking susceptibility of austenitic stainless steels SS304L, SS316L and SS904L was studied in an acidified seawater environment by slow strain rate testing at 24, 38 and 66...

Keywords/Search Tags:

Cracking susceptibility, Austenitic stainless

Related items

1	Study On Solidification Cracking Susceptibility Of Single-phase Austenitic Alloys During Laser Welding
2	The Evaluation Of Ductility Dip Cracking Susceptibility In Austenitic Stainless Steel During The Process Of Hot Working
3	Research On The Stress Corrosion Cracking Susceptibility Of The Stainless Steel With Surface Nanocrystallization By Small Punch Test
4	Susceptibility of 420 martensitic stainless steel to cracking in hydrogen sulfide/carbon dioxide/chloride environments
5	Study On Stress Corrosion Cracking Of Austenitic Stainless Steels In Chloride Solution
6	Mechanistic studies of stress-corrosion cracking in austenitic stainless steels and in copper-zinc alloys
7	Research On Stress Corrosion Cracking Of Typical Pressure Vessel Steels In Wet Hydrogen Sulfide Service
8	Experimental Study On Edge-cracking In Low-Nickel Austenitic Stainless Steel During Hot Rolling
9	Investigation Of Relatonship Between Martensite And Pitting Susceptibility Of Austenitic 304 Stainless Steel
10	A Study On Electrochemical And Mechanical Properties In Stress Corrosion Cracking Prediction Model For Austenitic Stainless Steels Used In Nuclear Power Plants