Porous materials as high performance adsorbents for CO2 capture, gas separation and purification

Global warming resulted from greenhouse gases emission has received a widespread attention. Among the greenhouse gases, CO2 contributes more than 60% to global warming due to its huge emission amount. The flue gas contains about 15% CO2 with N2 as the balance. If CO2 can be separated from flue gas, the benefit is not only reducing the global warming effect, but also producing pure CO2 as a very useful industry raw material. Substantial progress is urgent to be achieved in an industrial process. Moreover, energy crisis is one of the biggest challenges for all countries due to the short life of fossil fuels, such as, petroleum will run out in 50 years and coal will run out in 150 years according to today's speed. Moreover, the severe pollution to the environment caused by burning fossil fuels requires us to explore sustainable, environment-friendly, and facile energy sources. Among several alternative energy sources, natural gas is one of the most promising alternative energy sources due to its huge productivity, abundant feed stock, and ease of generation.;In order to realize a substantial adsorption process in industry, synthesis of new adsorbents or modification of existing adsorbent with improved properties has become the most critical issue. This dissertation reports systemic characterization and development of five serials of novel adsorbents with advanced adsorption properties.;In chapter 2, nitrogen-doped Hypercross-linking Polymers (HCPs) have been synthesized successfully with non-carcinogenic chloromethyl methyl ether (CME) as the cross-linking agent within a single step. Texture properties, surface morphology, CO2/N2 selectivity, and adsorption heat have been presented and demonstrated properly. A comprehensive discussion on factors that affect the CO2 adsorption and CO2/N 2 separation has also been presented. It was found that high micropore proportion and N-content could effectively enhance CO2 uptake and CO2/N2 separation selectivity.;In chapter 3, a new series of oxygen-doped ACs were synthesized from polyfuran. Different factors that affect the AC formation were investigated, and two kinds of porogens (ZnC12 and KOH) and two active temperatures (600 and 800 °C) were tested. At 298K and 1bar, an excellent selectivity for separating CO2/N2 (41.7) and CO2/CH 4(6.8) gas mixture pairs was obtained on the PF-600 KOH. A breakthrough simulation was also performed to demonstrate the potential of industrial applications. The PF-600 KOH sample showed the best separation result in the simulated adsorption breakthrough as well.;In chapter 4, quinone and hydroquinone on the surface of PF-600 ZnC1 2 were integrated. Significantly pore size shrinkage, improved CO 2/N2 and CO2/CH4 IAST selectivity were observed, which is 58.7% and 28.4 % higher than pristine porous carbon at 298K and 1 atm, respectively. In addition, transient breakthrough simulations for CO2/CH4/N2 binary mixtures were conducted in order to demonstrate the good separation performance in fixed bed adsorbers.;In chapter 5, a novel nitrogen doped polymer poly(2-phenyl-1,3,6,8tetraazacyclodecane) will be used as the precursor to produce microporous N-doped activated carbons. Three activation temperatures (600, 700, and 800 °C) has been investigated with KOH as the porogen. High nitrogen content has been remained in the resultant carbon materials. Improved CO2 adsorption capacity and selectivites for the separation of CO2/CH4/N2 binary gas mixtures were achieved by the carbon adsorbents due to their N-containing groups, narrow pore size distribution, and large specific surface area.;In chapter 6, MOF-derived activated carbons are developed from MIL-100(Al) as hard-template. Direct carbonization of MIL-100, MIL-100(Al)/F-127 composite, and MIL-100(Al)/KOH mixture has been investigated. Pore structure and surface morphology have been demonstrated. CO2/CH4/N2 binary selectivity, adsorption heats, and kinetic selectivity have been calculated. Breakthrough simulation has been conducted to mimic industrial application. We found that resultant carbons showed better CO2 capture ability and selectivity than parental MIL-100(Al).