| The bulk-heterojunction organic (BHJ) photovoltaics (OPVs) and lithium ion battery (LiB) have been extensively studied. Power conversion efficiency (PCE) of an OPV greater than 10% and utilizing group 4 elements as the anode to accommodate high capacity for LiBs are the goals of many studies. However, the currently ubiquitous hole-collecting layer of OPVs limit device performance and durability, and group 4 elements are unstable and brittle to be commercially produced. Thus, my thesis has focused on developing functional and durable interfacial layers (IFLs) for OPVs and characterizing flexible artificial solid-electrolyte interphase (SEI) for LiBs.;In Chapter 2, a series of robust organosilane-based dipolar self-assembled monolayer (SAM) IFLs on the tin-doped indium oxide (ITO) anodes of OPVs are developed. These hydrophobic and amorphous IFLs modify anode work functions from 4.66 to 5.27 eV. Two series of Glass/ITO/SAM IFL/Active Layer/LiF/Al BHJ OPVs are fabricated, and a strong positive correlation between the electrochemically-derived heterogeneous electron transport rate constants (ks) and OPV PCEs are observed due to enhanced anode carrier extraction.;In Chapter 3, a series of unusually denser organosilane-based SAM IFLs on ITO anodes of OPVs are developed. Precursor mixtures having short and long tail groups were simultaneously deposited to minimize sterical encumbrance and denser SAM IFLs are achieved. These heterogeneous supersaturated SAMs (SHSAMs), with PCE (7.62%) exceeding that of PEDOT:PSS IFL, are found to be 17% denser and enhances PCE by 54% versus comparable devices with homogeneous SAM IFLs due to enhanced charge selectivity and collection.;In Chapter 4, libraries of electron affinities (EAs) of widely used conductive polymers are constructed by cyclic voltammetry (CV) in conventional and LiB media. The EAs of the conductive polymer films measured via CV in conventional (EAC) and Li+ battery (EAB) media could be linearly correlated by EAB = (1.07 +/- 0.13) x EAC + (2.84 +/- 0.22)V. The slope and the intercept are correlated to the dielectric constants encompassing the polymer film and the redox potential of the reference electrode affected by the surrounding electrolyte, respectively. |