Investigating the stability of cathode materials for rechargeable lithium ion batteries

Lithium ion batteries are widely used in portable electronic devices and electric vehicles. However, safety is one of the most important issues for the Li-ion batteries' use. Some cathode materials, such as LiCoO 2, are thermally unstable in the charged state. Upon decomposition these cathode materials release O2, which could react with organic electrolyte, leading to a thermal runaway. Thus understanding the stability of the cathode materials is critical to the safety of lithium ion batteries.;Olivine-type LiMnPO4 is a promising cathode material for lithium ion batteries because of its high energy density. We have revealed the critical role of carbon in the stability and thermal behaviour of olivine MnPO 4 obtained by chemical delithiation of LiMnPO4. (Li)MnPO 4 samples with various particle sizes and carbon contents were studied. Carbon-free LiMnPO4 obtained by solid state synthesis in O 2 becomes amorphous upon delithiation. Small amounts of carbon (0.3 wt.%) help to stabilize the olivine structure, so that completely delithiated crystalline olivine MnPO4 can be obtained. Larger amount of carbon (2 wt.%) prevents full delithiation. Heating in air, O2, or N 2 results in structural disorder (< 300 °C), formation of an intermediate sarcopside Mn3(PO4)2 phase (350 -- 450 °C), and complete decomposition to Mn2P2O 7 on extended heating at 400 °C. Carbon protects MnPO4 from reacting with environmental water, which is detrimental to its structural stability.;We not only studied the crystalline olivine MnPO4, but also investigated the amorphous products obtained from carbon-free LiMnPO 4. We have revealed the Mn dissolution phenomenon during chemical delithiation of LiMnPO4, which causes the amorphization of olivine MnPO 4. Properties of crystalline-MnPO4 obtained from carbon-coated LiMnPO4 and of amorphous product resulting from the delithiation of pure LiMnPO4 were studied and compared. The P-rich amorphous phases in the latter are considered to be MnHP2O7 and MnH2P2O7 from XAS and XPS analysis.;Safety of batteries not only depends on the stability of the active materials, but also the interactions between the active materials and electrolyte. Thus we study the stability between the cathode materials and the electrolyte. The thermal stability of electrochemically delithiated Li0.1N 0.8C0.15Al0.05O2 (NCA), FePO4 (FP), Mn0.8Fe0.2PO4 (MFP), hydrothermally synthesized VOPO4, LiVOPO4 and electrochemically lithiated Li2VOPO4 is investigated by differential scanning calorimetry (DSC) and thermogravimetric analysis, coupled with mass spectrometry (TGA-MS). The thermal stability is found in the order: NCA< VOPO4< MFP< FP=LiVOPO4=Li2VOPO4. Sealed capsule high pressure experiments show a phase transformation of VOPO4 → HVOPO4 → H2VOPO4 when VOPO4 reacts with electrolyte (1 M LiPF6 in EC: DMC=1:1) between 200 and 300 °C.;Finally, we characterize the lithium storage and release mechanism of V2O5 aerogels by x-ray photoelectron spectroscopy (XPS). We study the influence of n--butyllithium (n--BuLi) treatments on the electrochemical performance of the aerogel. In addition to fully reversible V reduction and oxidation due to the intercalation reaction, we observe the formation of LiOH species that are only partially reversible. This is attributed to reaction with the interlayer water and is considered responsible for the gradual capacity fade. The n--BuLi treated aerogels display a higher capacity than those without and our XPS analysis reveals an additional reversible formation of Li2O.