| The present research was directed at adequate prediction of the temperature, deformation behavior (roll force, flow stress, strain and strain rate) and microstructural evolution (recovery, recrystallization, grain growth, austenite and ferrite grain sizes) during rolling in the Compact Strip Production (CSP) process, as well as the final mechanical properties of the hot rolled strips. This was accomplished with the aid of integrated process modeling, involving mathematical simulation, laboratory experiments and industrial campaigns. The study covered two conventional plain carbon steel grades, the A36 (AISI 1018, 0.17C-0.74Mn) and DQSK (AISI 1005, 0.038C-0.3Mn), and a range of plain carbon steel grades (0.06-0.09 C, 0.16-0.9 Mn) produced at HYLSA's CSP mill at Monterrey, Mexico.; In the laboratory, compression tests (both single and double-hits) were carried out on the Gleeble 1500 thermomechanical simulator in order to elucidate the effect of coarse austenite grain size on the flow stress and recrystallization behavior of the plain carbon steels. It was found that coarse grain size not only decreased the flow stress at a given strain but also substantially reduced the tendency toward dynamic recrystallization. An increase in grain size from 244 to 1110 {dollar}mu{dollar}m which is typical of the first stands of a conventional finishing mill and CSP hot-strip mill respectively, resulted in up to a 30 MPa decrease in the flow stress of both A36 and DQSK steel grades at similar operating conditions of temperature, strain and strain rate.; In order to validate the model and laboratory results with mill measurements from an operating CSP plant, an industrial trial was carried out at HYLSA's CSP mill in Monterrey, Mexico. During the industrial campaign, intermediate temperature measurements were made, CSP slab and coil samples were acquired, and all measured and recorded mill data and practices were obtained.; Comprehensive mathematical modeling of the rolling process was carried out employing finite difference and finite element analysis. The CSP mill measurements were utilized to validate model predictions of temperature, roll force, grain size and mechanical properties. Good agreement was obtained between prediction and measurement in most of the cases. An estimate of the heat extraction from the various mill sub-units was conducted from the validated calculations. It was found that heat loss by radiation accounted for 48-51 percent of the total heat loss, the work rolls accounted for 41-44 percent, the descaling unit accounted for 4-6 percent and the interstand sprays accounted for the remaining 3-4 percent. It was found that the uniform strain model consistently predicts lower temperatures than the target exit temperature for thin gauges due to a low estimate of deformation heat. Model results captured the details of heat transfer, deformation, recrystallization and austenite decomposition in the CSP mill. The effect of various mill parameters were elucidated, and the similarities and differences between conventional cold-charge rolling and CSP rolling were highlighted. (Abstract shortened by UMI.)... |