| GaN and related nitrides are promising materials for applications as UV/blue light emitters and in high-power, high-temperature electonic devices. Unfortunately, the vast potential of these materials cannot be realized effectively due to a large density of threading dislocations, arising from large lattice mismatch between GaN and utilized substrates. Therefore, a new approach to the heteroepitaxial growth is desirable, and a compliant substrate might help to remedy the situation.; A modified model for the compliant substrate consisting of the compliant membrane glued to a thick handling substrate by a soft layer was proposed. We have chosen 6H-SiC as a starting substrate and ion implantation as a means of creating a buried layer.; High fluence ion implantation of different species in 6H-SiC was performed at elevated temperatures and damage removal/accumulation was studied. It was found that temperatures around 1600°C are necessary to successfully recrystallize the radiation damage for Ti, Ga, Si and C implantations, but no damage removal was monitored for In implantation. In order to minimize the damage produced during ion implantation, it was decided to employ a multistep process in which each implantation step was followed by annealing. This approach was realized for 125 keV Ti++ and 300 keV Ga+ implantations up to a total dose of 1.8 × 1017 cm–2. Ti-implanted substrates were shown to retain good quality in the top layer, whereas Ga implantation preserves the quality of the near-surface region only at lower doses. The implanted species concentration was monitored after each step using Rutherford Backscattering (RBS). GaN films were grown on the prepared substrates and a control SiC sample by MOCVD. TEM and photoluminescence measurements have demonstrated that the quality of GaN films improves upon growth on compliant substrates. |