Carbon nanofiber reinforced epoxy matrix composites and syntactic foams - mechanical, thermal, and electrical properties

The tailorability of composite materials is crucial for use in a wide array of real-world applications, which range from heat-sensitive computer components to fuselage reinforcement on commercial aircraft. The mechanical, electrical, and thermal properties of composites are highly dependent on their material composition, method of fabrication, inclusion orientation, and constituent percentages. The focus of this work is to explore carbon nanofibers (CNFs) as potential nanoscale reinforcement for hollow particle filled polymer composites referred to as syntactic foams. In the present study, polymer composites with high weight fractions of CNFs, ranging from 1-10 wt.%, are used for quasi-static and high strain rate compression analysis, as well as for evaluation and characterization of thermal and electrical properties. It is shown that during compressive characterization of vapor grown carbon nanofiber (CNF)/epoxy composites in the strain rate range of 10-4-2800 s-1, a difference in the fiber failure mechanism is identified based on the strain rate. Results from compression analyses show that the addition of fractions of CNFs and glass microballoons varies the compressive strength and elastic modulus of epoxy composites by as much as 53.6% and 39.9%. The compressive strength and modulus of the syntactic foams is also shown to generally increase by a factor of 3.41 and 2.96, respectively, with increasing strain rate when quasi-static and high strain rate testing data are compared, proving strain rate sensitivity of these reinforced composites. Exposure to moisture over a 6 month period of time is found to reduce the quasi-static and high strain rate strength and modulus, with a maximum of 7% weight gain with select grades of CNF/syntactic foam. The degradation of glass microballoons due to dealkalization is found to be the primary mechanism for reduced mechanical properties, as well as moisture diffusion and weight gain. In terms of thermal analysis results, the coefficient of thermal expansion (CTE) of CNF/epoxy and CNF/syntactic foam composites reinforced with glass microballoons decrease by as much as 11.6% and 38.4%. The experimental CTE values for all of the composites also fit within the bounds of established analytical models predicting the CTE of fiber and particle-reinforced composites. Further thermal studies through dynamic mechanical analysis demonstrated increased thermal stability and damping capability, where the maximum use and glass transition temperatures increase as much as 27.1% and 25.0%, respectively. The electrical properties of CNF reinforced composites are evaluated as well, where the electrical impedance decreases and the dielectric constant increases with addition of CNFs. Such behavior occurs despite the presence of epoxy and glass microballoons, which serve as insulative phases. Such results are useful in design considerations of lightweight composite materials used in weight saving, compressive strength, and damage tolerance applications, such as lightweight aircraft structure reinforcement, automobile components, and buoyancy control with marine submersibles. The results of the analyses have also evaluated certain factors for environmental exposure and temperature extremes, as well as considerations for electronics packaging, all of which have also played a role in shaping avant-garde composite structure designs for efficient, versatile, and long-life service use.