The isothermal section of the phase diagram of the Gd-Co-V ternary system at 773K was investigated by X-ray powder diffraction(XRD),metallographic analysis,electron probe microanalysis,and differential thermal analysis(DTA) techniques.The isothermal section consists of 14 single-phase regions,26 two-phase regions and 13 three-phase regions.The solid solubility of V in the compounds Co17Gd2,Co3Gd,Co2Gd,Co7Gd12and CoGd3 were about 11.0,2.0, 6.0,1.2 and 5.3 at.%V,respectively.It was found that there are some homogeneity range in the only ternary compound of GdCo12-xVx with x = 2.6 to 3.7 at 773K.No other ternary compound has been observed.No solubility of Gd in compounds Co3V,σCoV or CoV3 was observed.There is no solubility of V in Co7Gd2 or Co3Gd4 observed at 773K.Co5Gd was not found at 773K.It was confirmed that the compound Co7Gd12exists at 773K by XRD and DTA techniques.
|