Superconducting properties and vortex dynamics of bismuth strontium calcium copper oxide nanoribbons with and without periodic array of nanoscale holes

The distinguishing features of high-temperature superconducting materials are the dynamics of vortex matter in the mixed state which are greatly affected by the high anisotropy and the Josephson coupling between layers. Experiments have focused on investigating melting and dynamic phases of vortex matter with random pinning. However, the advancements in sample preparation techniques have made it possible to investigate the vortex matter with periodic pinnings, since it can serve as a model system to study periodic elastic media such as electron crystals driven on substrates with arrays of defects. It also offers the possibility to increase the critical current of a superconductor through a matching effect which represents itself as peaks (dips) in the field dependences of the critical current (magnetoresisance). This effect is due to the enhanced pinning strength at matching fields where the density of the flux quanta is equal to or multiple times that of the pins. This dissertation reports investigation on the dynamics of vortex matter with periodic pinning array by utilizing BSCCO-2212 crystalline nanoribbons containing periodic arrays of nanoscale holes. Systematic transport measurements reveal the existence of possible intermediate phases of a soft solid and/or a mixture of solid and liquid during melting for the melting transition from solid to a pure liquid. The results of this research demonstrate that the matching effect can be an effective tool in revealing the nature of various vortex phases during melting transition.;In addition, anomalous resistive peaks below Tc and the effect of magnetic field orientation on superconductivity of BSCCO-2212 nanoribbons with array of nanoscale holes are also investigated. Angle-dependent magnetoresistances are scaled as H=Hthetacostheta. Therefore, only the perpendicular component of the magnetic field affects the superconductivity. Moreover, layers in BSCCO nanoribbons are lying in the a-b plane parallel to each other. Moreover, at large currents and fields, the resistance shows a non-monotonic dependence on temperature, even showing values that are higher than the normal state resistance for certain ranges of parameters. Observed behavior is attributed to the brick-wall morphology of the nanoribbons leading to a competition between normal and superconductive tunneling that is known to take place in granular superconductive systems.